Effective strategy for enhancing the activity and durability of gas diffusion electrode in high-temperature polymer electrolyte membrane fuel cells: In-situ growth of Pt nanowires on dual microporous layers

Author

Listed:
  • Zhang, Weiqi
  • Chen, Yuan
  • Jin, Yuan
  • Liu, Huiyuan
  • Ma, Qiang
  • Xu, Qian
  • Su, Huaneng

Abstract

High-temperature polymer electrolyte membrane fuel cells (HT-PEMFCs) suffer from high platinum (Pt) loading and limited lifetime issues due to the low Pt efficiency of the conventional electrode and poor durability of Pt/C catalyst under harsh operating conditions. Thus, dual microporous layer (MPL) structured gas diffusion layers were developed, utilizing formic acid reduction for the in-situ growth of Pt nanowires (NWs). The optimal ratio of the hydrophilic and hydrophobic MPLs was determined to be 1:1. The resulting Pt NWs gas diffusion electrode (GDE) achieved a significantly high Pt mass-specific peak power density, which was 2.48 times higher than the conventional Pt/C GDE. After accelerated degradation tests, the peak power density and the electrochemically active surface area of Pt NWs GDE decreased by 10.84 % and 4.47 %, respectively, significantly lower than those of the conventional Pt/C GDE. The superior activity and durability of Pt NWs GDE are attributed to its binder-free characteristic, the outstanding activity and stability of one-dimensional Pt NWs, and the strong adherent force between the in-situ grown Pt and the carbon substrate. This study provides a straightforward and effective strategy to reduce the Pt loading and enhance electrode durability, thereby facilitating the large-scale application of HT-PEMFCs.

Suggested Citation

  • Zhang, Weiqi & Chen, Yuan & Jin, Yuan & Liu, Huiyuan & Ma, Qiang & Xu, Qian & Su, Huaneng, 2024. "Effective strategy for enhancing the activity and durability of gas diffusion electrode in high-temperature polymer electrolyte membrane fuel cells: In-situ growth of Pt nanowires on dual microporous ," Energy, Elsevier, vol. 308(C).
    • Handle: RePEc:eee:energy:v:308:y:2024:i:c:s0360544224026689
    DOI: 10.1016/j.energy.2024.132894
    as

    Download full text from publisher

    File URL: http://www.sciencedirect.com/science/article/pii/S0360544224026689
    Download Restriction: Full text for ScienceDirect subscribers only
    File URL: https://libkey.io/10.1016/j.energy.2024.132894?utm_source=ideas
    LibKey link: if access is restricted and if your library uses this service, LibKey will redirect you to where you can use your library subscription to access this item
    ---><---

    As the access to this document is restricted, you may want to search for a different version of it.

    References listed on IDEAS

    as
    1. Authayanun, Suthida & Saebea, Dang & Patcharavorachot, Yaneeporn & Arpornwichanop, Amornchai, 2014. "Effect of different fuel options on performance of high-temperature PEMFC (proton exchange membrane fuel cell) systems," Energy, Elsevier, vol. 68(C), pages 989-997.
    2. Ribeirinha, P. & Alves, I. & Vázquez, F. Vidal & Schuller, G. & Boaventura, M. & Mendes, A., 2017. "Heat integration of methanol steam reformer with a high-temperature polymeric electrolyte membrane fuel cell," Energy, Elsevier, vol. 120(C), pages 468-477.
    3. Guo, Xinru & Guo, Yumin & Wang, Jiangfeng & Meng, Xin & Deng, Bohao & Wu, Weifeng & Zhao, Pan, 2023. "Thermodynamic analysis of a novel combined heating and power system based on low temperature solid oxide fuel cell (LT-SOFC) and high temperature proton exchange membrane fuel cell (HT-PEMFC)," Energy, Elsevier, vol. 284(C).
    4. Xuan, Lingfeng & Wang, Yancheng & Lan, Jinwei & Tao, Kai & Zhou, Caiying & Mei, Deqing, 2023. "Development of cathode ordered membrane electrode assembly based on TiO2 nanowire array and ultrasonic spraying," Energy, Elsevier, vol. 264(C).
    5. Shahgaldi, Samaneh & Ozden, Adnan & Li, Xianguo & Hamdullahpur, Feridun, 2020. "A scaled-up proton exchange membrane fuel cell with enhanced performance and durability," Applied Energy, Elsevier, vol. 268(C).
    Full references (including those not matched with items on IDEAS)

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Gabriele Loreti & Andrea Luigi Facci & Stefano Ubertini, 2021. "High-Efficiency Combined Heat and Power through a High-Temperature Polymer Electrolyte Membrane Fuel Cell and Gas Turbine Hybrid System," Sustainability, MDPI, vol. 13(22), pages 1-24, November.
    2. Abdollahzadeh, M. & Ribeirinha, P. & Boaventura, M. & Mendes, A., 2018. "Three-dimensional modeling of PEMFC with contaminated anode fuel," Energy, Elsevier, vol. 152(C), pages 939-959.
    3. Yang, Yue & Yuan, Songmei & Liu, Jieyuan & Zhang, Zikang & Lu, Tie, 2024. "Effect of catalyst ink particle size on the structure of the catalyst layer and electrical performance in the process of ultrasonic spray manufacturing PEMFCs," Energy, Elsevier, vol. 294(C).
    4. Chen, Ben & Cai, Yonghua & Tu, Zhengkai & Chan, Siew Hwa & Wang, Jun & Yu, Yi, 2017. "Gas purging effect on the degradation characteristic of a proton exchange membrane fuel cell with dead-ended mode operation I. With different electrolytes," Energy, Elsevier, vol. 141(C), pages 40-49.
    5. Li, Yanju & Li, Dongxu & Ma, Zheshu & Zheng, Meng & Lu, Zhanghao & Song, Hanlin & Guo, Xinjia & Shao, Wei, 2022. "Performance analysis and optimization of a novel vehicular power system based on HT-PEMFC integrated methanol steam reforming and ORC," Energy, Elsevier, vol. 257(C).
    6. Konstantinos Kappis & Joan Papavasiliou & George Avgouropoulos, 2021. "Methanol Reforming Processes for Fuel Cell Applications," Energies, MDPI, vol. 14(24), pages 1-30, December.
    7. Yu, Bor-Chern & Wang, Yi-Chun & Lu, Hsin-Chun & Lin, Hsiu-Li & Shih, Chao-Ming & Kumar, S. Rajesh & Lue, Shingjiang Jessie, 2017. "Hydroxide-ion selective electrolytes based on a polybenzimidazole/graphene oxide composite membrane," Energy, Elsevier, vol. 134(C), pages 802-812.
    8. Wang, Yufei & Wang, Kaichen & Yu, Zhangying & Ye, Feng & Feng, Yuancheng & Xiao, Feng & Zhang, Lifang & Xu, Chao & Liu, Guicheng & Liu, Jianguo, 2024. "Insights to the differences in catalytic performance of under-rib and under-channel regions for PEM water electrolysis," Renewable Energy, Elsevier, vol. 235(C).
    9. Jianuo Chen & Xuekun Lu & Lingtao Wang & Wenjia Du & Hengyi Guo & Max Rimmer & Heng Zhai & Yuhan Liu & Paul R. Shearing & Sarah J. Haigh & Stuart M. Holmes & Thomas S. Miller, 2024. "Laser scribed proton exchange membranes for enhanced fuel cell performance and stability," Nature Communications, Nature, vol. 15(1), pages 1-18, December.
    10. Han, Zepeng & Han, Wei & Sui, Jun, 2024. "Exergo-environmental cost optimization and thermodynamic analysis for a solar-driven combined heating and power system," Energy, Elsevier, vol. 302(C).
    11. Han, Li & Wang, Shiqi & Cheng, Yingjie & Chen, Shuo & Wang, Xiaojing, 2024. "Multi-timescale scheduling of an integrated electric-hydrogen energy system with multiple types of electrolysis cells operating in concert with fuel cells," Energy, Elsevier, vol. 307(C).
    12. Ribeirinha, P. & Alves, I. & Vázquez, F. Vidal & Schuller, G. & Boaventura, M. & Mendes, A., 2017. "Heat integration of methanol steam reformer with a high-temperature polymeric electrolyte membrane fuel cell," Energy, Elsevier, vol. 120(C), pages 468-477.
    13. Ribeirinha, P. & Abdollahzadeh, M. & Sousa, J.M. & Boaventura, M. & Mendes, A., 2017. "Modelling of a high-temperature polymer electrolyte membrane fuel cell integrated with a methanol steam reformer cell," Applied Energy, Elsevier, vol. 202(C), pages 6-19.
    14. Liu, Jiaran & Tan, Jinzhu & Yang, Weizhan & Li, Yang & Wang, Chao, 2021. "Better electrochemical performance of PEMFC under a novel pneumatic clamping mechanism," Energy, Elsevier, vol. 229(C).
    15. Ji-Woong Jeon & Jun-Geon Park & Geon-Hyeop Kim & Seung-Heon Lee & Jeong-Woo Shin & Gu-Young Cho, 2025. "Analysis of Electrochemical Properties of LT-SOFCs According to Thickness of PrO x Cathode Interlayer," Sustainability, MDPI, vol. 17(4), pages 1-17, February.
    16. Perng, Shiang-Wuu & Chien, Tsai-Chieh & Horng, Rong-Fang & Wu, Horng-Wen, 2019. "Performance enhancement of a plate methanol steam reformer by ribs installed in the reformer channel," Energy, Elsevier, vol. 167(C), pages 588-601.
    17. De Masi, Rosa Francesca & Festa, Valentino & Penchini, Daniele & Ruggiero, Silvia & Tariello, Francesco & Vanoli, Giuseppe Peter & Zinno, Alberto, 2024. "State of art of hydrogen utilization for building sector and set-up with preliminary experimental results of 1 kWel solid oxide fuel cell installed in a nearly zero energy house," Energy, Elsevier, vol. 302(C).
    18. Zhang, Jun & Zhang, Caizhi & Li, Jin & Deng, Bo & Fan, Min & Ni, Meng & Mao, Zhanxin & Yuan, Honggeng, 2021. "Multi-perspective analysis of CO poisoning in high-temperature proton exchange membrane fuel cell stack via numerical investigation," Renewable Energy, Elsevier, vol. 180(C), pages 313-328.
    19. Singdeo, Debanand & Dey, Tapobrata & Gaikwad, Shrihari & Andreasen, Søren Juhl & Ghosh, Prakash C., 2017. "A new modified-serpentine flow field for application in high temperature polymer electrolyte fuel cell," Applied Energy, Elsevier, vol. 195(C), pages 13-22.
    20. Hyunyong Lee & Inchul Jung & Gilltae Roh & Youngseung Na & Hokeun Kang, 2020. "Comparative Analysis of On-Board Methane and Methanol Reforming Systems Combined with HT-PEM Fuel Cell and CO 2 Capture/Liquefaction System for Hydrogen Fueled Ship Application," Energies, MDPI, vol. 13(1), pages 1-25, January.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:eee:energy:v:308:y:2024:i:c:s0360544224026689. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: Catherine Liu (email available below). General contact details of provider: http://www.journals.elsevier.com/energy .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.