Optimization of B2O3 coating process for NCA cathodes to achieve long-term stability for application in lithium ion batteries

Author

Listed:
  • Chen, Jiasheng
  • Wang, Xuan Liang
  • Jin, En Mei
  • Moon, Seung-Guen
  • Jeong, Sang Mun

Abstract

Ni-rich cathodes exhibit rapid capacity degradation upon cycling; hence, the development of Ni-rich cathode materials with a stable electrochemical performance for use in next-generation lithium-ion batteries (LIBs) are extremely challenging. In this study, boron trioxide (B2O3)-modified LiNi0.87Co0.10Al0.03O2 (NCA) compounds with high charging–discharging structural stability were prepared using the Ni0.88Co0.095Al0.025OH precursor for application in LIB cathodes. In addition, the sintering temperature of the NCA cathode material was optimized. B2O3 not only filled in the cracks that formed during the first sintering process but also effectively prevented the fragmentation and loss of cathode NCA particles during the charge–discharge process, thus improving their electrochemical properties. The coated particles exhibited sufficient structural integrity and did not exhibit severe cracking during the cycling process. The B2NCA3 cathode with 2.0 wt% B2O3 demonstrated sufficient cyclic stability and rate properties. It exhibited a high specific capacity of 184 mAh g−1 and a capacity retention of 86% after 100 cycles at 0.2 C and 25 °C.

Suggested Citation

  • Chen, Jiasheng & Wang, Xuan Liang & Jin, En Mei & Moon, Seung-Guen & Jeong, Sang Mun, 2021. "Optimization of B2O3 coating process for NCA cathodes to achieve long-term stability for application in lithium ion batteries," Energy, Elsevier, vol. 222(C).
    • Handle: RePEc:eee:energy:v:222:y:2021:i:c:s0360544221001626
    DOI: 10.1016/j.energy.2021.119913
    as

    Download full text from publisher

    File URL: http://www.sciencedirect.com/science/article/pii/S0360544221001626
    Download Restriction: Full text for ScienceDirect subscribers only
    File URL: https://libkey.io/10.1016/j.energy.2021.119913?utm_source=ideas
    LibKey link: if access is restricted and if your library uses this service, LibKey will redirect you to where you can use your library subscription to access this item
    ---><---

    As the access to this document is restricted, you may want to search for a different version of it.

    References listed on IDEAS

    as
    1. Zhang, Fan & Jia, Zirui & Wang, Chao & Feng, Ailing & Wang, Kuikui & Hou, Tianqi & Liu, Jiajia & Zhang, Yi & Wu, Guanglei, 2020. "Sandwich-like silicon/Ti3C2Tx MXene composite by electrostatic self-assembly for high performance lithium ion battery," Energy, Elsevier, vol. 195(C).
    2. Pengfei Yan & Jianming Zheng & Jian Liu & Biqiong Wang & Xiaopeng Cheng & Yuefei Zhang & Xueliang Sun & Chongmin Wang & Ji-Guang Zhang, 2018. "Tailoring grain boundary structures and chemistry of Ni-rich layered cathodes for enhanced cycle stability of lithium-ion batteries," Nature Energy, Nature, vol. 3(7), pages 600-605, July.
    3. Han, Jinduo & Jia, Yongzhong & Jin, Shan & Jing, Yan & Tillard, Monique & Belin, Claude, 2006. "Morphology and electrochemistry of spinel Li–Mn–O optimized by composite technology," Energy, Elsevier, vol. 31(12), pages 2088-2093.
    Full references (including those not matched with items on IDEAS)

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Jianwen Liang & Yuanmin Zhu & Xiaona Li & Jing Luo & Sixu Deng & Yang Zhao & Yipeng Sun & Duojie Wu & Yongfeng Hu & Weihan Li & Tsun-Kong Sham & Ruying Li & Meng Gu & Xueliang Sun, 2023. "A gradient oxy-thiophosphate-coated Ni-rich layered oxide cathode for stable all-solid-state Li-ion batteries," Nature Communications, Nature, vol. 14(1), pages 1-12, December.
    2. Tang, Hong & Jiang, Mengjin & Ren, Erhui & Zhang, Yue & Lai, Xiaoxu & Cui, Ce & Jiang, Shouxiang & Zhou, Mi & Qin, Qin & Guo, Ronghui, 2020. "Integrate electrical conductivity and Li+ ion mobility into hierarchical heterostructure Ti3C2@CoO/ZnO composites toward high-performance lithium ion storage," Energy, Elsevier, vol. 212(C).
    3. Jung-Hui Kim & Ju-Myung Kim & Seok-Kyu Cho & Nag-Young Kim & Sang-Young Lee, 2022. "Redox-homogeneous, gel electrolyte-embedded high-mass-loading cathodes for high-energy lithium metal batteries," Nature Communications, Nature, vol. 13(1), pages 1-11, December.
    4. Yang, Zunxian & Meng, Qing & Guo, Zaiping & Yu, Xuebin & Guo, Tailiang & Zeng, Rong, 2013. "Highly reversible lithium storage in uniform Li4Ti5O12/carbon hybrid nanowebs as anode material for lithium-ion batteries," Energy, Elsevier, vol. 55(C), pages 925-932.
    5. Chia-Hsin Lin & Senthil-Kumar Parthasarathi & Satish Bolloju & Mozaffar Abdollahifar & Yu-Ting Weng & Nae-Lih Wu, 2022. "Synthesis of Micron-Sized LiNi 0.8 Co 0.1 Mn 0.1 O 2 and Its Application in Bimodal Distributed High Energy Density Li-Ion Battery Cathodes," Energies, MDPI, vol. 15(21), pages 1-15, October.
    6. Jin, En Mei & Kim, Min Soo & Kim, Tae Yun & Shin, Beom-Ju & Moon, Jong-Ho & Jeong, Sang Mun, 2023. "Upcycling of silicon scrap collected from photovoltaic cell manufacturing process for lithium-ion batteries via transferred arc thermal plasma," Energy, Elsevier, vol. 262(PB).
    7. Minglei Mao & Xiao Ji & Qiyu Wang & Zejing Lin & Meiying Li & Tao Liu & Chengliang Wang & Yong-Sheng Hu & Hong Li & Xuejie Huang & Liquan Chen & Liumin Suo, 2023. "Anion-enrichment interface enables high-voltage anode-free lithium metal batteries," Nature Communications, Nature, vol. 14(1), pages 1-13, December.
    8. Su, Laisuo & Choi, Paul & Nakamura, Nathan & Charalambous, Harry & Litster, Shawn & Ilavsky, Jan & Reeja-Jayan, B., 2021. "Multiscale operando X-ray investigations provide insights into electro-chemo-mechanical behavior of lithium intercalation cathodes," Applied Energy, Elsevier, vol. 299(C).
    9. Gogwon Choe & Hyungsub Kim & Jaesub Kwon & Woochul Jung & Kyu-Young Park & Yong-Tae Kim, 2024. "Re-evaluation of battery-grade lithium purity toward sustainable batteries," Nature Communications, Nature, vol. 15(1), pages 1-10, December.
    10. Weng, Guoming & Su, Yuzhi & Liu, Zhaoqing & Zhang, Jianhua & Dong, Wen & Xu, Changwei, 2009. "Electrochemical properties of novel organodisulfide poly 1,2-bis(thiophen-3-ylmethyl)disulfane as cathode material for secondary lithium batteries," Energy, Elsevier, vol. 34(9), pages 1351-1354.
    11. Junbo Zhang & Haikuo Zhang & Suting Weng & Ruhong Li & Di Lu & Tao Deng & Shuoqing Zhang & Ling Lv & Jiacheng Qi & Xuezhang Xiao & Liwu Fan & Shujiang Geng & Fuhui Wang & Lixin Chen & Malachi Noked & , 2023. "Multifunctional solvent molecule design enables high-voltage Li-ion batteries," Nature Communications, Nature, vol. 14(1), pages 1-14, December.
    12. Yi Pei & Qing Chen & Meiyu Wang & Pengjun Zhang & Qingyong Ren & Jingkai Qin & Penghao Xiao & Li Song & Yu Chen & Wen Yin & Xin Tong & Liang Zhen & Peng Wang & Cheng-Yan Xu, 2022. "A medium-entropy transition metal oxide cathode for high-capacity lithium metal batteries," Nature Communications, Nature, vol. 13(1), pages 1-13, December.
    13. Ruixia Chu & Yujian Zou & Peidong Zhu & Shiwei Tan & Fangyuan Qiu & Wenjun Fu & Fu Niu & Wanyou Huang, 2022. "Progress of Single-Crystal Nickel-Cobalt-Manganese Cathode Research," Energies, MDPI, vol. 15(23), pages 1-32, December.
    14. Tongchao Liu & Lei Yu & Jun Lu & Tao Zhou & Xiaojing Huang & Zhonghou Cai & Alvin Dai & Jihyeon Gim & Yang Ren & Xianghui Xiao & Martin V. Holt & Yong S. Chu & Ilke Arslan & Jianguo Wen & Khalil Amine, 2021. "Rational design of mechanically robust Ni-rich cathode materials via concentration gradient strategy," Nature Communications, Nature, vol. 12(1), pages 1-10, December.
    15. Christian M. Julien & Alain Mauger, 2020. "NCA, NCM811, and the Route to Ni-Richer Lithium-Ion Batteries," Energies, MDPI, vol. 13(23), pages 1-46, December.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:eee:energy:v:222:y:2021:i:c:s0360544221001626. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: Catherine Liu (email available below). General contact details of provider: http://www.journals.elsevier.com/energy .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.