Power evolution of fuel cell stack driven by anode gas diffusion layer degradation

Author

Listed:
  • Yang, Yange
  • Li, Xiang
  • Tang, Fumin
  • Ming, Pingwen
  • Li, Bing
  • Zhang, Cunman

Abstract

Recent research has revealed that gas diffusion layer degradation has a crucial effect on fuel cell stack power density evolution. There have been several investigations focused on the influence of cathode gas diffusion layer degradation on stack performance. However, the degradation behavior and contribution of the anode gas diffusion layer on stack output power remain to be studied. Here, the 1000 h durability test of a stack was conducted under the New European Driving Cycle condition, and the effect of anode gas diffusion layer failure on the stack output power was evaluated. Carbon corrosion is the main attenuation characteristic of the anode gas diffusion layer, which significantly reduces its mechanical strength, and decreased the support capacity of the anode gas diffusion layer. Moreover, carbon corrosion also leads to exposure of new hydrophilic surfaces, reducing the hydrophobicity of the gas diffusion layer. In addition, the loss of hydrophobic agents is also one of the main characteristics of anode gas diffusion layer attenuation, which is the main reason for hydrophobicity loss. The decreased hydrophobicity will significantly improve the water retention capacity, and reduce the back diffusion of cathode water. As a result, mass transfer resistance will increase at a high current density. In conclusion, we verified the crucial impact of anode gas diffusion layer on cell output power density, and provide a new idea for the stack power attenuation investigation.

Suggested Citation

  • Yang, Yange & Li, Xiang & Tang, Fumin & Ming, Pingwen & Li, Bing & Zhang, Cunman, 2022. "Power evolution of fuel cell stack driven by anode gas diffusion layer degradation," Applied Energy, Elsevier, vol. 313(C).
    • Handle: RePEc:eee:appene:v:313:y:2022:i:c:s030626192200294x
    DOI: 10.1016/j.apenergy.2022.118858
    as

    Download full text from publisher

    File URL: http://www.sciencedirect.com/science/article/pii/S030626192200294X
    Download Restriction: Full text for ScienceDirect subscribers only
    File URL: https://libkey.io/10.1016/j.apenergy.2022.118858?utm_source=ideas
    LibKey link: if access is restricted and if your library uses this service, LibKey will redirect you to where you can use your library subscription to access this item
    ---><---

    As the access to this document is restricted, you may want to search for a different version of it.

    References listed on IDEAS

    as
    1. Taghiabadi, Mohammad Mohammadi & Zhiani, Mohammad & Silva, Valter, 2019. "Effect of MEA activation method on the long-term performance of PEM fuel cell," Applied Energy, Elsevier, vol. 242(C), pages 602-611.
    2. Lee, Yongtaek & Kim, Bosung & Kim, Yongchan & Li, Xianguo, 2011. "Degradation of gas diffusion layers through repetitive freezing," Applied Energy, Elsevier, vol. 88(12), pages 5111-5119.
    3. Yang, Yange & Zhou, Xiangyang & Li, Bing & Zhang, Cunman, 2021. "Failure of cathode gas diffusion layer in 1 kW fuel cell stack under new European driving cycle," Applied Energy, Elsevier, vol. 303(C).
    4. Chu, Tiankuo & Zhang, Ruofan & Wang, Yanbo & Ou, Mingyang & Xie, Meng & Shao, Hangyu & Yang, Daijun & Li, Bing & Ming, Pingwen & Zhang, Cunman, 2021. "Performance degradation and process engineering of the 10 kW proton exchange membrane fuel cell stack," Energy, Elsevier, vol. 219(C).
    5. Wang, Yun & Chen, Ken S. & Mishler, Jeffrey & Cho, Sung Chan & Adroher, Xavier Cordobes, 2011. "A review of polymer electrolyte membrane fuel cells: Technology, applications, and needs on fundamental research," Applied Energy, Elsevier, vol. 88(4), pages 981-1007, April.
    6. Kurnia, Jundika C. & Sasmito, Agus P. & Shamim, Tariq, 2019. "Advances in proton exchange membrane fuel cell with dead-end anode operation: A review," Applied Energy, Elsevier, vol. 252(C), pages 1-1.
    7. Liu, Zhiyang & Chen, Jian & Liu, Hao & Yan, Chizhou & Hou, Yang & He, Qinggang & Zhang, Jiujun & Hissel, Daniel, 2020. "Anode purge management for hydrogen utilization and stack durability improvement of PEM fuel cell systems," Applied Energy, Elsevier, vol. 275(C).
    Full references (including those not matched with items on IDEAS)

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Yang, Yange & Zhou, Xiangyang & Li, Bing & Zhang, Cunman, 2021. "Failure of cathode gas diffusion layer in 1 kW fuel cell stack under new European driving cycle," Applied Energy, Elsevier, vol. 303(C).
    2. Chen, Dongfang & Pei, Pucheng & Ren, Peng & Song, Xin & Wang, He & Zhang, Lu & Wang, Mingkai, 2022. "Analytical methods for the effect of anode nitrogen concentration on performance and voltage consistency of proton exchange membrane fuel cell stack," Energy, Elsevier, vol. 258(C).
    3. Yang, Daijun & Lan, Yilin & Chu, Tiankuo & Li, Bing & Ming, Pingwen & Zhang, Cunman & Zhou, Xiangyang, 2022. "Rapid activation of a full-length proton exchange membrane fuel cell stack with a novel intermittent oxygen starvation method," Energy, Elsevier, vol. 260(C).
    4. Yin, Cong & Song, Yating & Liu, Meiru & Gao, Yan & Li, Kai & Qiao, Zemin & Tang, Hao, 2022. "Investigation of proton exchange membrane fuel cell stack with inversely phased wavy flow field design," Applied Energy, Elsevier, vol. 305(C).
    5. Niu, Zhiqiang & Bao, Zhiming & Wu, Jingtian & Wang, Yun & Jiao, Kui, 2018. "Two-phase flow in the mixed-wettability gas diffusion layer of proton exchange membrane fuel cells," Applied Energy, Elsevier, vol. 232(C), pages 443-450.
    6. Mohideen, Mohamedazeem M. & Liu, Yong & Ramakrishna, Seeram, 2020. "Recent progress of carbon dots and carbon nanotubes applied in oxygen reduction reaction of fuel cell for transportation," Applied Energy, Elsevier, vol. 257(C).
    7. Zhang, Jikai & Wang, Changjian & Zhang, Aifeng, 2022. "Experimental study on temperature and performance of an open-cathode PEMFC stack under thermal radiation environment," Applied Energy, Elsevier, vol. 311(C).
    8. Liu, Shihua & Li, Xiaoyang & Pang, Linjia & Geng, Tie & Guo, Yonggang & Jiang, Lin & Kang, Kejia & Wang, Xinchao & Liu, Zongyao, 2022. "Study on the effect of purging time on the performance of PEMFC with dead-ended anode under gravity," Renewable Energy, Elsevier, vol. 200(C), pages 1141-1151.
    9. Li, Bing & Wan, Kechuang & Xie, Meng & Chu, Tiankuo & Wang, Xiaolei & Li, Xiang & Yang, Daijun & Ming, Pingwen & Zhang, Cunman, 2022. "Durability degradation mechanism and consistency analysis for proton exchange membrane fuel cell stack," Applied Energy, Elsevier, vol. 314(C).
    10. Yuemeng Zhang & Jia Wang & Zhanhui Yao, 2023. "Recent Development of Fuel Cell Core Components and Key Materials: A Review," Energies, MDPI, vol. 16(5), pages 1-23, February.
    11. Jung, Guo-Bin & Chuang, Kai-Yuan & Jao, Ting-Chu & Yeh, Chia-Chen & Lin, Chih-Yuan, 2012. "Study of high voltage applied to the membrane electrode assemblies of proton exchange membrane fuel cells as an accelerated degradation technique," Applied Energy, Elsevier, vol. 100(C), pages 81-86.
    12. Yang, Yange & Li, Xiang & Chu, Tiankuo & Li, Bing & Zhang, Cunman, 2022. "Property evolution of gas diffusion layer and performance shrink of fuel cell during operation," Renewable Energy, Elsevier, vol. 194(C), pages 596-603.
    13. Wang, Yujie & Sun, Zhendong & Li, Xiyun & Yang, Xiaoyu & Chen, Zonghai, 2019. "A comparative study of power allocation strategies used in fuel cell and ultracapacitor hybrid systems," Energy, Elsevier, vol. 189(C).
    14. Peng, Fei & Zhao, Yuanzhe & Li, Xiaopeng & Liu, Zhixiang & Chen, Weirong & Liu, Yang & Zhou, Donghua, 2017. "Development of master-slave energy management strategy based on fuzzy logic hysteresis state machine and differential power processing compensation for a PEMFC-LIB-SC hybrid tramway," Applied Energy, Elsevier, vol. 206(C), pages 346-363.
    15. Zhang, Xiaoqing & Yang, Jiapei & Ma, Xiao & Zhuge, Weilin & Shuai, Shijin, 2022. "Modelling and analysis on effects of penetration of microporous layer into gas diffusion layer in PEM fuel cells: Focusing on mass transport," Energy, Elsevier, vol. 254(PA).
    16. Liao, Shuxin & Qiu, Diankai & Yi, Peiyun & Peng, Linfa & Lai, Xinmin, 2022. "Modeling of a novel cathode flow field design with optimized sub-channels to improve drainage for proton exchange membrane fuel cells," Energy, Elsevier, vol. 261(PB).
    17. Zheng Huang & Laisuo Su & Yunjie Yang & Linsong Gao & Xinyu Liu & Heng Huang & Yubai Li & Yongchen Song, 2023. "Three-Dimensional Simulation on the Effects of Different Parameters and Pt Loading on the Long-Term Performance of Proton Exchange Membrane Fuel Cells," Sustainability, MDPI, vol. 15(4), pages 1-22, February.
    18. Vasallo, Manuel Jesús & Bravo, José Manuel & Andújar, José Manuel, 2013. "Optimal sizing for UPS systems based on batteries and/or fuel cell," Applied Energy, Elsevier, vol. 105(C), pages 170-181.
    19. Bae, Suk Joo & Kim, Seong-Joon & Lee, Jin-Hwa & Song, Inseob & Kim, Nam-In & Seo, Yongho & Kim, Ki Buem & Lee, Naesung & Park, Jun-Young, 2014. "Degradation pattern prediction of a polymer electrolyte membrane fuel cell stack with series reliability structure via durability data of single cells," Applied Energy, Elsevier, vol. 131(C), pages 48-55.
    20. Yan, Peijian & Tian, Pengfei & Cai, Cheng & Zhou, Shenghu & Yu, Xinhai & Zhao, Shuangliang & Tu, Shan-Tung & Deng, Chengwei & Sun, Yi, 2020. "Antioxidative and stable PdZn/ZnO/Al2O3 catalyst coatings concerning methanol steam reforming for fuel cell-powered vehicles," Applied Energy, Elsevier, vol. 268(C).

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:eee:appene:v:313:y:2022:i:c:s030626192200294x. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: Catherine Liu (email available below). General contact details of provider: http://www.elsevier.com/wps/find/journaldescription.cws_home/405891/description#description .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.