Tribological Properties of ZrO2 Coating on the Ball Joint of an Axial Piston Pump in High Water-Based Emulsion Medium

This paper studies the tribological properties of the ZrO 2 -coated spherical joint pair of the axial piston pump in a high water-based emulsion medium. Firstly, atmospheric plasma spraying was used to prepare the ZrO 2 coating on the surface of the spherical joint pair. Secondly, the tribological characteristics of the steel-steel pair and ceramic-ceramic pair were analyzed by the friction and wear testing machine under the conditions of a high water-based emulsion concentration, load size, and load frequency. White light interference three-dimensional surface profiler and scanning electron microscope were used to analyze the original and worn surfaces of the samples, and then the friction and wear of the different material pairs were discussed. The results show that the friction reduction and wear resistance of the ceramic ball joint are superior to those of the steel ball joint. When the load is 100 N, the frequency is 1 Hz, and the emulsion concentration is 5%, and the friction coefficient and wear loss of the ceramic-ceramic ball joint pair are the lowest. The emulsion concentration and load have great influence on the friction coefficient and wear amount, while the frequency has little influence on them. With increasing concentration of the emulsion, the friction coefficient decreases and tends to be stable, but with increasing of load, the friction coefficient and wear increase. The friction coefficient and wear loss of the ceramic-ceramic ball joint in pure water are 0.25 times higher than those of the steel ball joint under the same working conditions. Therefore, when the concentration of the high water-based emulsion is 5%, 100 N load, 1 Hz frequency, the ceramic-ceramic ball joints display the best friction and wear resistance of the two. The research results provide a theoretical basis for the design, manufacture, and application of the ceramic coating hydraulic components in a high water-based emulsion medium.