Assessment of the Structural Integrity of a Laser Weld Joint of Inconel 718 and ASS 304L

For high-temperature industries operating at nearly 750 °C (advanced ultra-super critical boilers), dissimilar welding between Inconel alloys and austenitic stainless steel (ASS) are commonly adopted. The high-temperature resistive properties of Inconel and ASS alloys are highly qualified for high-temperature applications. In this experimental study, dissimilar autogenous laser beam welding (LBW) between Inconel 718 and ASS 304L is investigated. This paper explains the detailed study on the microstructural and mechanical behavior of the LBW dissimilar joint. The microstructural study indicates the presence of laves phases in the weld zone. Additionally, the weld zone shows heterogeneous microstructural formation, owing to the non-uniform welding heat in the different areas of the weld zone. The optical images show the presence of mixed dendrites, i.e., equiaxed, cellular, and columnar morphology, in the weld zone and in the fusion zones of either side. The energy-dispersive spectroscopy (EDS) results show the presence of segregated elements (Nb, Mo, Cr, and Ti) at the weld center. These segregated elements are the reason for the occurrence of the laves phases in the weld zone. The presence of Nb and Mo may form the laves phase (Fe, Ni, Cr) 2 (Nb, Mo, Ti) along with Fe, Ni and Cr. The presence of an unmixed zone is observed in the HAZ of the Inconel 718, whereas the HAZ of the ASS 304L shows the presence of an unmixed zone (UZ) and a partially mixed zone (PMZ), as observed on the optical and SEM images. To obtain the mechanical properties of the laser weld, the tensile test, microhardness test, and impact test were measured at room temperature. The tensile specimens show a brittle failure at the ASS 304L side, which was initiated from the weld top, with average tensile stress of 658.225 MPa. The reason for the ASS 304L fracture is because of the presence of UZ and PMZ, and the lower hardness value of the ASS side. The UZ and PMZ lead to the fracture of the tensile specimen along the ASS 304L side’s HAZ. The measurement of microhardness carried out along the transverse length indicates an average microhardness of 214.4 HV, and the value is 202.9 HV along the weld depth. The mixed morphology of the microstructure promotes the variation in hardness in both directions. The hardness along the length shows a high hardness value in the weld zone and uniformly decreases along the base materials. The Charpy impact test of the weld zone shows the brittle fracture of the impact specimens. From the microstructural and mechanical results, the LBW dissimilar weld between Inconel 718 and ASS 304L is qualified for safe use in high-temperature end applications, such as AUSC power plants.