Performance Evaluation of Asphalt Concrete Incorporating Steel Slag Powder as Filler under the Combined Damage of Temperature and Moisture

Recycling steel slag into asphalt concrete is an important way to save natural resources and protect the environment. The high asphalt absorption and adsorption and the sensitivity of steel slag aggregate (SSA) to the combined damage of temperature and moisture (volume expansion and poor durability under freeze-thaw cycle damage) still pose risks for the use of SSA in asphalt concrete. It is urgent to develop new utilization methods of steel slag. With this in mind, the material properties of steel slag powder (SSP) and performance characteristics of asphalt concrete incorporating SSP filler were evaluated in this research. The SSP was prepared in the laboratory by grinding steel slag with a particle size of 2.36–4.75 mm. Firstly, the material properties of SSP including the specific surface area, particle gradation, apparent density, chemical compositions, and thermal stability were analyzed. Steel slag (2.36–4.75 mm) and common limestone powder (LP) filler were used as control groups. The grindability of steel slag and the advantages of using SSP as a filler in asphalt concrete were preliminarily analyzed based on the test results of material properties. Then, the Superpave method was used to design asphalt concrete incorporating SSP and LP. Considering that steel slag is sensitive to the combined damage of temperature and moisture, the main engineering performance of asphalt concrete after the combined damage of temperature and moisture was evaluated to further reveal the feasibility of using SSP as a filler. Two combined damage modes, namely hot water damage and freeze-thaw cycle damage, were applied. Results suggest that although the steel slag is more difficult to grind compared to limestone particles, grinding steel slag into SSP has improved the uniformity of its material properties. Good uniformity of material properties, high alkalinity, and excellent thermal stability of SSP give it some advantages in its application in asphalt concrete. Although the freeze-thaw cycle damage has a slightly more significant effect on the engineering performance of asphalt concrete than hot water damage, compared to the asphalt concrete with LP filler, even after freeze-thaw cycle damage for three cycles asphalt concrete incorporating SSP still possesses comparable or better volume stability, mechanical performance, high-temperature deformation resistance, low-temperature crack resistance, fatigue crack resistance, and fatigue durability.