Multi-Scale Characterization of Porosity and Cracks in Silicon Carbide Cladding after Transient Reactor Test Facility Irradiation

Author

Listed:
  • Fei Xu

    (Idaho National Laboratory, Idaho Falls, ID 83415, USA)

  • Tiankai Yao

    (Idaho National Laboratory, Idaho Falls, ID 83415, USA)

  • Peng Xu

    (Idaho National Laboratory, Idaho Falls, ID 83415, USA)

  • Jason L. Schulthess

    (Idaho National Laboratory, Idaho Falls, ID 83415, USA)

  • Mario D. Matos

    (Idaho National Laboratory, Idaho Falls, ID 83415, USA)

  • Sean Gonderman

    (General Atomics, San Diego, CA 92121, USA)

  • Jack Gazza

    (General Atomics, San Diego, CA 92121, USA)

  • Joshua J. Kane

    (Ultra Safe Nuclear Corporation, Seattle, WA 98199, USA)

  • Nikolaus L. Cordes

    (Los Alamos National Laboratory, Los Alamos, NM 87545, USA)

Abstract

Silicon carbide (SiC) ceramic matrix composite (CMC) cladding is currently being pursued as one of the leading candidates for accident-tolerant fuel (ATF) cladding for light water reactor applications. The morphology of fabrication defects, including the size and shape of voids, is one of the key challenges that impacts cladding performance and guarantees reactor safety. Therefore, quantification of defects’ size, location, distribution, and leak paths is critical to determining SiC CMC in-core performance. This research aims to provide quantitative insight into the defect’s distribution under multi-scale characterization at different length scales before and after different Transient Reactor Test Facility (TREAT) irradiation tests. A non-destructive multi-scale evaluation of irradiated SiC will help to assess critical microstructural defects from production and/or experimental testing to better understand and predict overall cladding performance. X-ray computed tomography (XCT), a non-destructive, data-rich characterization technique, is combined with lower length scale electronic microscopic characterization, which provides microscale morphology and structural characterization. This paper discusses a fully automatic workflow to detect and analyze SiC-SiC defects using image processing techniques on 3D X-ray images. Following the XCT data analysis, advanced characterizations from focused ion beam (FIB) and transmission electron microscopy (TEM) were conducted to verify the findings from the XCT data, especially quantitative results from local nano-scale TEM 3D tomography data, which were utilized to complement the 3D XCT results. In this work, three SiC samples (two irradiated and one unirradiated) provided by General Atomics are investigated. The irradiated samples were irradiated in a way that was expected to induce cracking, and indeed, the automated workflow developed in this work was able to successfully identify and characterize the defects formation in the irradiated samples while detecting no observed cracking in the unirradiated sample. These results demonstrate the value of automated XCT tools to better understand the damage and damage propagation in SiC-SiC structures for nuclear applications.

Suggested Citation

  • Fei Xu & Tiankai Yao & Peng Xu & Jason L. Schulthess & Mario D. Matos & Sean Gonderman & Jack Gazza & Joshua J. Kane & Nikolaus L. Cordes, 2023. "Multi-Scale Characterization of Porosity and Cracks in Silicon Carbide Cladding after Transient Reactor Test Facility Irradiation," Energies, MDPI, vol. 17(1), pages 1-15, December.
  • Handle: RePEc:gam:jeners:v:17:y:2023:i:1:p:197-:d:1310140
    as

    Download full text from publisher

    File URL: https://www.mdpi.com/1996-1073/17/1/197/pdf
    Download Restriction: no

    File URL: https://www.mdpi.com/1996-1073/17/1/197/
    Download Restriction: no
    ---><---

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:gam:jeners:v:17:y:2023:i:1:p:197-:d:1310140. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    We have no bibliographic references for this item. You can help adding them by using this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: MDPI Indexing Manager (email available below). General contact details of provider: https://www.mdpi.com .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.