Anticorrosive Efficiency of the AISI 316 SS in Sustainable Ecological Concrete Manufactured with SCBA-SF Exposed to Magnesium Sulphate

In this research, it was evaluated the anticorrosive efficiency of AISI 316 SS embedded in Sustainable Ecological Concrete (SEC) manufactured with partial substitutions of Portland Cement by combinations of SCBA and SF in 10%, 20%, and 30%. For the electrochemical evaluation, the Sustainable Ecological Concretes (SEC) were exposed to solution at 3.5% of MgSO4, these aggressive ions are found in soils, industrial or marine environments and that interact with the civil works that are built in these places. The dosage or proportioning of the Sustainable Ecological Concrete (SEC) mixtures was carried out as indicated by ACI 211.1. The anticorrosive efficiency of the AISI 316 SS was evaluated through the tests of the potential of corrosion (Ecorr) and corrosion rate (Icorr) during a period of 180 days of exposition to the aggressive medium. The values of Ecorr indicate in the AISI 316 SS a 10% of corrosion risk and uncertainty at the end of monitoring, according to the norm ASTM C-876-15, in all the mixtures, but the values of Icorr in the specimens manufactured with SEC indicate resistance to sulfate corrosion more than 10 times compared to conventional concrete and AISI 1018 steel.