Synthesis And Morphological Control Of Monodispersed Microsized Ceria Particles
The morphological control of crystalline cerium oxide particles was realized by homogeneous precipitation process followed by calcination in air at 400°C. The effects of room temperature pre-aging time on the morphologies of final products were investigated. Monodispersed rod-like cerium carbonate precursor was produced at 70°C for 2 h using the solution without pre-aging treatment. In contrast, monodispersed spherical precursor and plate-like precursor were obtained under the same conditions after pre-aging the solution at 25°C for 72 and 144 h, respectively. Ceria particles with similar morphologies and particle size to those of carbonate precursor could be obtained after calcination in air at 400°C. The monodispersed spherical, rod-like, and plate-like cerium oxide particles were successfully synthesized.
If you experience problems downloading a file, check if you have the proper application to view it first. In case of further problems read the IDEAS help page. Note that these files are not on the IDEAS site. Please be patient as the files may be large.
As the access to this document is restricted, you may want to look for a different version under "Related research" (further below) or search for a different version of it.
Volume (Year): 17 (2010)
Issue (Month): 02 ()
|Contact details of provider:|| Web page: http://www.worldscinet.com/srl/srl.shtml|
|Order Information:|| Email: |
When requesting a correction, please mention this item's handle: RePEc:wsi:srlxxx:v:17:y:2010:i:02:p:147-152. See general information about how to correct material in RePEc.
For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: (Tai Tone Lim)
If references are entirely missing, you can add them using this form.